3LPE triple layer of polyethylene

V.I.P. Pesaro is one of the few companies able to offer the 3LPE coating on pipes as well as on custom pieces.
The coating is a multilayer composed of a primer fusion bonded epoxy (FBE) followed by an adhesive copolymer and another layer of polyethylene which provides resistance and long-lasting protection.
The system ensures the applicability of the sintered coating also on pieces with special shapes.

Long-lasting corrosion protection
The FBE primer offers an excellent adhesion to the substrate and provides a long-term corrosion protection for pipelines operating at moderate temperatures.
It also ensures the resistance to the cathodic disbondment so the total cost of cathodic protection of the pipeline decreases.

Remarkable mechanical protection
The applied polyethylene layer protects the pipeline during shipping and installation reducing repair costs and providing a protection underground against mechanical, chemical and abrasive attacks.
Applying an higher polyethylene thickness the mechanical protection increases proportionally.

Other advantages of the sintered system
V.I.P. Pesaro using this special application technique is able to coat also specific pieces with special shapes (bends, tees, reducers, joints, etc.).
There aren’t any limitations about the amount of pieces to coat, even the single piece can be treated.
3LPE can be applied in different thicknesses to meet the requirements of project specifications.

  • Small and large pipes
  • Standard fittings
  • Wide radius bends
  • Special fittings

Diameter from 1/2” to 120”
Maximum unit length 13.5 meters
Maximum unit weight 15,000 kg.

Joints and/or custom pieces: (bends, tees, reducers, flanges, etc.)
Maximum size 3.0 x 3.0 x 13.5 meters
Maximum unit weight 15,000 kg
Maximum thickness of the coating 3,5 mm.

  • Preparing and testing: oven pre-heating, blasting, testing
  • Anticorrosive coating / Sintering: oven pre-heating, FBE spray powder
  • Adhesive layer: spray adhesive, oven baking
  • Top coat: PE spray powder, oven baking, air cooling
  • Check, storage and delivery: testing, packing, ready for shipment

*Sintering is the coating process where a coating powder is sprayed on a preheated piece. Thanks to the heat emitted from the surface the powder fuses creating an homogeneous and continuous layer.

Selected from among the top qualified international brands by the biggest companies
DIN 30670
UNI EN ISO 21809-1
NF A 49-710

for additional standards, please contact the technical office.

ISO 9001, ISO 14001, OHSAS 18001
  • Specific Gravity PE: 0.943 g/cm3
  • Elongation at Break ISO 527: > 300%
  • Hardness: Shore D 52
  • Minimum recommended temperature: – 40°C
  • Maximum recommended temperature: + 80°C
3LPE - Triple Layer Polyethylene
3LPE - Triple Layer Polyethylene

3LPE Production system – From analysis to shipment

V.I.P. Pesaro takes care of customers needs designing custom coatings for special pieces in order to always satisfy clients expectations. Since more than ten years we are providing our protective solutions worldwide.
We offer specific consultancy since the analyses of project requirements. We design the best solution selecting with the client the most suitable coating and the best applicable technique. After realization, we carry out laboratory tests to truly guarantee a perfect results.

3LPE Product specifications

Property Test Description Typical Values
Degree of cure of epoxy resin DIN 30670 ∆Tg according to the manufacturer specifications
Impact DIN 30670 ≥ 7 J/mm
Cathodic Disbondment DIN 30670 23°C/ 28 days or 60°C/ 2 days max 7 mm
Peel Strenght DIN 30670 > 35 N/cm at 23°C; < 15 N/cm at 70°C
3LPE Three layers polyethylene

See our online presentation, please CLICK HERE TO READ IT.

FBE (Fusion Bonded Epoxy) is the best epoxy resin powder applied on pre‐heated surfaces. Thermosetting coating designed for the anticorrosive protection of articles destined to immersion or buried services in oil and gas sector and in the protection of the water pipeline.